ANALISA PENGARUH VARIASI KONSENTRASI PELAPISAN POLYSILAZANE PADA PERMUKAAN SUDU TURBIN SS 410 DALAM PENINGKATAN SIFAT MEKANIK
Kata Kunci:
polysilazane, korosi, sudu tubin uapAbstrak
The steam turbine blade is the main component in the steam turbine which experiences
wear due to friction with the flowing hot fluid. Apart from that, turbine blades also
experience corrosion due to the acid content contained in the steam and erosion due to
high pressure. To overcome this problem, the surface of the steam turbine blade will be
coated with organic and inorganic polysilazane. Tests that will be carried out to determine
the performance of the polysilazane layer on the turbine blade include hardness testing with a pencil hardness test, analyzing the adhesion of the coating with the Cross Cut Adhesion test and to determine the adhesive strength of the film formed from the polysilazane reaction using a scanning electron microscope on the substrate.
Abstrak
Sudu turbin uap adalah komponen utama dalam turbin uap yang mengalami keausan
akibat gesekan dengan fluida panas yang mengalir. Selain itu sudu turbin juga
mengalami korosi akibat kandungan asam yang terkandung pada uap dan erosi akibat
tekanan tinggi. Untuk mengatasi masalah tersebut, permukaan sudu turbin uap akan
dilapisi dengan Organik dan Inorganik Polysilazane. Pengujian yang akan dilakukan untuk
mengetahui performa lapisan polisilazane pada sudu turbin antara lain pengujian kekerasan dengan pencil hardness test, menganalisa daya rekat lapisan dengan Cross Cut Adhesion test dan untuk mengetahui daya rekat film yang terbentuk dari reaksi polysilazane melalui scanning electronmicroscope terhadap substrat.